Titanium Grade 9 Technical Report
Grade 9 titanium is also know as Ti-3AL-2.4V or simply Ti-3-2.5. Grade 9 is grouped in with the commercially pure grades because it is cold rollable. Grade 9 strengths fall between Grade 4 and Grade 5. It has excellent corrosion resistance and is used in aerospace and industrial applications. Grade 9 can be used at higher temperatures than Grades 1 through 4.
Chemical Composition |
| Element |
Grade 9 |
| Nitrogen, MAX |
0.03 |
| Carbon, MAX |
0.08 |
| Hydrogen, MAX |
0.015 |
| Iron, MAX |
0.25 |
| Oxygen, MAX |
0.15 |
| Aluminum |
2.5-3.5 |
| Vanadium |
2.0-3.0 |
| Tin |
…. |
| Palladium |
…. |
| Chromium |
…. |
| Molybdenum |
…. |
| Zirconium |
…. |
| Nickel |
…. |
| Residuals (each) max |
0.10 |
| Residuals (total) max |
0.40 |
| Titanium |
Remainder |
|
|
| Mechanical Properties:
|
| Titanium and Titanium Alloy Strip, Sheet, and Plate |
| Tensile Requirements |
| Grade |
Tensile Strength |
Yield Strength, 0.2 % Offset |
Elongation in 2 in. or 50 mm |
Bend Test |
| min |
min |
max |
Under 0.070 in (1.8 mm) in T. |
0.070 to 0.187 in (1.8–4.75 mm) in T. |
| ksi |
Mpa |
ksi |
Mpa |
ksi |
Mpa |
min, % |
| 9 |
90 |
620 |
70 |
483 |
... |
... |
15D |
5T |
6T |
|
|
| Titanium and Titanium Alloy Bars and Billets |
| Tensile Requirements |
| Grade |
Tensile Strength min |
Yield Strength (0.2 % Offset) |
Elongation |
Reduction of Area |
| ksi |
Mpa |
ksi |
Mpa |
min % |
min % |
| 9 |
90 |
620 |
70 |
483 |
15 |
25 |
|
|
| Titanium and Titanium Alloy Forgings |
| Grade |
Tensile Strength min |
Yield Strength (0.2 % Offset) |
Elongation |
Reduction of Area |
| ksi |
Mpa |
ksi |
Mpa |
min % |
min % |
| 9 |
120 |
828 |
110 |
759 |
10 |
25 |
|
|
| Titanium and Titanium Alloy Seamless Pipe |
| Grade |
Tensile Strength |
Yield Strength, 0.2 % Offset |
Elongation in 2 in. or 50 mm gage length, |
| min |
min |
max |
| ksi |
Mpa |
ksi |
Mpa |
ksi |
Mpa |
min, % |
| 9 |
90 |
620 |
70 |
483 |
... |
... |
10 |
|
|
| Titanium and Titanium Alloy Wire |
| Grade |
Tensile Strength |
Yield Strength, 0.2 % Offset |
Elongation |
| min |
min |
| ksi |
Mpa |
ksi |
Mpa |
min, % |
| 9 |
90 |
620 |
70 |
483 |
15 |
|
|
|
|
|
|