High strength titanium alloy sheet is formed at room temperature

Titanium plate is widely recognized for its high strength, light weight and good structural rigidity. High-strength titanium alloy ti-6al-4v can be used not only in aviation, but also as an important candidate material for structural parts in automobile, chemical industry and other industrial fields. The formability of ti-6al-4v alloy sheet at room temperature is very limited, and the springback after forming is very large, which brings many problems to traditional stamping and pressure forming. Although the forming limit of ti-6al-4v alloy sheet at high temperature will be increased and the springback will be reduced, room-temperature forming still has great advantages in cost saving.

Rolling forming is a kind of forming method in which the metal blank is gradually deformed by the rotating roll, which is suitable for the structural parts with high forming strength and limited formability. Because the springback Angle of the material is small and can be compensated by a simple and easy method in the process of rolling forming, rolling forming is an effective method for ti-6al-4v alloy sheet forming at room temperature. Therefore, the scientific research personnel for after 820 ℃ annealing treatment of 2 mm thick high-strength Ti -6Al -4V alloy sheet forming and springback behavior at room temperature for laboratory research.
Find Better Metal for Better Future
Products
Zirconium
Titanium
Tantalum
Niobium
Molybdenum
Tungsten
Nickel
Others
Tel:+86 21 56836035
Fax:+86 21 56836035
Email:sales@northalloys.com
Address:No 188,Xinfeng Road,Shanghai China 201501
sales@northalloys.com
Copyright © 2024 North Alloys All Rights Reserved Tel:+86 21 56836035 | Overview | Products&Service | Technical Assistance | Appliance